ER308L不銹鋼焊絲廠家報價
ER308L | ER308L | H00Cr21Ni10 | 0.02 | 0.42 | 1.65 | 20.10 | 10.33 | - | - | |
ER309 | ER309 | H1Cr24Ni13 | 0.083 | 0.42 | 1.63 | 23.83 | 13.13 | - | - | |
ER309L | ER309L | H00Cr24Ni13 | 0.02 | 0.39 | 1.98 | 23.88 | 12.90 | - | - | |
ER309LSi | ER309LSi | - | 0.02 | 0.87 | 1.55 | 24.10 | 13.00 | - | - | |
ER310 | ER310 | H1Cr26Ni21 | 0.086 | 0.40 | 2.01 | 27.40 | 21.80 | - | - | |
ER316 | ER316 | H0Cr19Ni12Mo2 | 0.050 | 0.36 | 1.78 | 19.61 | 12.50 | 5.49 | - | |
ER316L | ER316L | H00Cr19Ni12Mo2 | 0.025 | 0.42 | 1.91 | 19.10 | 12.58 | 2.57 | - | |
ER316LSi | ER316LSi | - | 0.021 | 0.77 | 1.95 | 19.32 | 13.45 | 2.58 | - | |
ER317 | ER317 | H0Cr19Ni14Mo3 | 0.048 | 0.45 | 1.86 | 19.41 | 14.23 | 3.51 | - | |
ER317L | ER317L | H00Cr19Ni14Mo3 | 0.023 | 0.40 | 1.76 | 19.60 | 13.68 | 3.63 | - | |
ER HlCrl8Ni9Ti | - | H1Cr18Ni9Ti | 0.087 | 0.86 | 1.58 | 18.47 | 10.20 | - | Ti:0.62 | |
ER321 | ER321 | H0Cr20Ni10Ti | 0.062 | 0.49 | 1.74 | 19.50 | 9.57 | - | Ti:0.82 | |
ER·H0Cr21Ni10Ti | - | H0Cr21Ni10Ti | 0.057 | 0.41 | 1.86 | 20.31 | 9.72 | - | Ti:0.73 | |
ER·H0Cr18Ni9Ti | - | H0Cr18Ni9Ti | 0.053 | 0.57 | 1.27 | 18.61 | 10.20 | - | Ti:0.59 | |
ER347 | ER347 | H0Cr20Ni10Nb | 0.030 | 0.41 | 1.61 | 20.37 | 9.90 | - | Nb:0.80 | |
ER410 | ER410 | H1Cr13 | 0.100 | 0.45 | 0.43 | 11.81 | 0.17 | - | - | |
ER430 | ER430 | H1Cr17 | 0.038 | 0.39 | 0.46 | 16.37 | 0.20 | - | - | |
ER·H2Cr13 | - | H2Cr13 | 0.160 | 0.45 | 0.51 | 13.00 | 0.47 | - | - | |
不銹鋼焊絲的選用
MIG及TIG焊接方法主要以純Ar作為保護氣體，熔池中的合金氧化很少，使得焊接接頭具有優(yōu)異的綜合理化性能；但可能有損焊接效率。
不銹鋼的性能很大程度上取決于成分。不銹鋼埋弧焊絲的成份設(shè)計都考慮了由于焊接時合金的燒損。該系列焊絲的選擇應(yīng)以被焊母材成份為準(zhǔn)，選用相同的合金體系；焊絲成份盡量接近(等于或稍高于) 母材成份。合金體系的不同對不銹鋼性能 (如延展性、耐腐蝕性、抗裂性等) 影響是巨大的，應(yīng)關(guān)注。